Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.

     

Reducing web latency with coding-based fast multi-path loss recovery

Wireless Networks - TCP latency is critical to the performance of Web services. However, packet loss greatly impairs the TCP performance due to its poor loss recovery mechanisms. Recent work FUSO...     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

An index structure supporting rule activation in pervasive applications

World Wide Web - Rule mechanism has been widely used in many areas, such as databases, artificial intelligent and pervasive computing. In a rule mechanism, rule activation decides which rules are...     

浮选柱反浮选脱镁工艺研究

利用浮选柱对高硅镁中低品位胶磷矿(P_2O_5 25.74%、MgO 1.31%、SiO_2 13.79%)进行反浮选脱镁实验,优化了反浮选脱镁工艺,并比较了浮选柱和浮选机的反浮选脱镁效果。确定最佳脱镁工艺条件为:捕收剂用量1.2 kg·t~(-1)、磷酸用量7 kg·t~(-1)、充气流量600 L·h~(-1)、冲洗水流量6 L·h~(-1)、柱径比8,在此条件下,得到P_2O_5品位为27.36%、MgO含量为0.64%的精矿,且精矿产率为92.65%,P_2O_5回收率为98.71%。     

喷油方式对斜齿轮齿面温度的影响

为探讨喷油方式对齿面温度的影响，以斜齿轮为研究对象，通过CFD仿真和试验研究不同喷油方式对斜齿轮齿面温度的影响。针对斜齿轮喷油润滑过程的特点，分析其齿面摩擦生热量，简化轮齿喷油润滑计算模型，并基于CFX进行齿面对流换热仿真研究，得到了不同喷油方式下的齿面温度；基于功率开放式斜齿轮试验平台，对不同喷油方式下的齿面温度进行了试验测量，与仿真计算结果进行对比分析。结果表明：在高速重载斜齿轮传动系统中，啮出侧喷油润滑的方式比啮入侧喷油润滑方式的冷却降温效果要好。     

Synthesis of Ionic Ultramicroporous Polymers for Selective Separation of Acetylene from Ethylene

The design of highly stable and efficient porous materials is essential for developing breakthrough hydrocarbon separation methods based on physisorption to replace currently used energy-intensive distillation/absorption technologies. Efforts to develop advanced porous materials such as zeolites, coordination frameworks, and organic polymers have met with limited success. Here, a new class of ionic ultramicroporous polymers (IUPs) with high-density inorganic anions and narrowly distributed ultramicroporosity is reported, which are synthesized by a facile free-radical polymerization using branched and amphiphilic ionic compounds as reactive monomers. A covalent and ionic dual-crosslinking strategy is proposed to manipulate the pore structure of amorphous polymers at the ultramicroporous scale. The IUPs exhibit exceptional selectivity (286.1–474.4) for separating acetylene from ethylene along with high thermal and water stability, collaboratively demonstrated by gas adsorption isotherms and experimental breakthrough curves. Modeling studies unveil the specific binding sites for acetylene capture as well as the interconnected ultramicroporosity for size sieving. The porosity-engineering protocol used in this work can also be extended to the design of other ultramicroporous materials for the challenging separation of other key gas constituents.